Direct Electrospinning of Cellulose Acetate onto Polyurethane Sheet and Effect of Its Saponification on Mechanical Properties
| العنوان: | Direct Electrospinning of Cellulose Acetate onto Polyurethane Sheet and Effect of Its Saponification on Mechanical Properties |
|---|---|
| المؤلفون: | Ali, Md. Momotaz, Pakkang, Nutthira, Taira, Shogo, Koda, Keiichi, Itoyama, Koki, Uraki, Yasumitsu |
| بيانات النشر: | Taylor & Francis 2019-05-25 |
| نوع الوثيقة: | Electronic Resource |
| مستخلص: | This article reports on direct electrospinning of water-soluble cellulose acetate (WSCA) and cellulose diacetate (CDA) onto a non-conductive synthetic polymer sheet such as polyurethane (PU) sheet to modify its surface morphology. The direct electrospinning was successfully performed after spraying an anti-static agent on the PU sheet. Furthermore, tight fixation of the fibers was achieved by spraying a dimethylformamide/ethanol (1/1) solution during the spinning. Finally, the cellulose acetate fibers on the PU sheet were converted to regenerated cellulose fibers by saponification. Changes in surface morphology were evaluated via tribology tests. The friction coefficient of the PU sheet significantly decreased with increases in the amount of deposited fiber, thereby suggesting that the PU sheet surface became smoother. After saponification, the friction coefficients of the sheets slightly increased, with the exception of the PU sheet with the increased amount of saponified WSCA fibers, and this was potentially attributed to changes in the elasticity upon saponification. |
| مصطلحات الفهرس: | Electrospinning, cellulose acetate, polyurethane (PU) sheet, lamination, tribology test, 586, article (author version) |
| URL: | |
| الاتاحة: | Open access content. Open access content This is an Accepted Manuscript of an article published by Taylor & Francis in Journal of Wood Chemistry and Technology on 25 May 2019, available online: http://www.tandfonline.com/10.1080/02773813.2019.1590416 |
| ملاحظة: | English |
| Other Numbers: | YX@ oai:eprints.lib.hokudai.ac.jp:2115/78824 Journal of wood chemistry and technology, 39(4): 282-295 1197663184 |
| المصدر المساهم: | HOKKAIDO UNIV From OAIster®, provided by the OCLC Cooperative. |
| رقم الانضمام: | edsoai.on1197663184 |
| قاعدة البيانات: | OAIster |
| الوصف غير متاح. |