Mechanical alloying of iron-coated NbC and Si in stirred media mill
| العنوان: | Mechanical alloying of iron-coated NbC and Si in stirred media mill |
|---|---|
| المؤلفون: | Al-Azzawi A., Kristály F., Rácz Á., Baumli P., Bohács K., Mucsi G. |
| المصدر: | Journal of Mining and Metallurgy. Section B: Metallurgy, Vol 55, Iss 2, Pp 209-216 (2019) |
| بيانات النشر: | Technical Faculty, Bor, 2019. |
| سنة النشر: | 2019 |
| المجموعة: | LCC:Mining engineering. Metallurgy |
| مصطلحات موضوعية: | niobium carbide, silicon, mechanical alloying, nanostructure, phase composition, Mining engineering. Metallurgy, TN1-997 |
| الوصف: | In the current research, the effect of mechanical alloying (MA) of iron-coated NbC and Si on the material’s fineness and crystal structure was investigated. The MA experiments were carried out in a batch-type laboratory scale stirred media mill for various residence times up to 240 min in isopropanol. During MA, milling energy was measured, and stress energy (SE) was calculated. Morphology and material structural changes, during the mechanical alloying process, were determined by means of scanning electron microscopy (SEM) and powder X-ray diffraction (XRD), respectively. The particle size distribution of the product was measured by a Horiba 950 LA laser particle size analyser. Evolution of phases during highenergy milling of NbC, Al-Fe-carbide, Fe, and Si was studied as a function of specific milling energy. Transformations in the crystal structure were revealed, namely the generation of cementite and Nb-Si-carbide, which was proved by XRD results and thermodynamic calculations. As result of the experiments, optimum MA conditions were determined. The application of the mechanical alloying method gives the opportunity to produce nanocrystalline phase from the initial ironcoated NbC and Si powder |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | English |
| تدمد: | 1450-5339 2217-7175 |
| Relation: | https://doaj.org/toc/1450-5339; https://doaj.org/toc/2217-7175 |
| DOI: | 10.2298/JMMB181124016A |
| URL الوصول: | https://doaj.org/article/bf0ef4ee22844718a02bec0e68886e12 |
| رقم الانضمام: | edsdoj.bf0ef4ee22844718a02bec0e68886e12 |
| قاعدة البيانات: | Directory of Open Access Journals |
| تدمد: | 14505339 22177175 |
|---|---|
| DOI: | 10.2298/JMMB181124016A |