Academic Journal
The Bridgman method growth and spectroscopic characterization of calcium fluoride single crystals
| العنوان: | The Bridgman method growth and spectroscopic characterization of calcium fluoride single crystals |
|---|---|
| المؤلفون: | Elswie Ibrahim Hana, Lazarević Zorica Ž., Radojević Vesna, Gilić Martina, Rabasović Maja, Šević Dragutin, Romčević Nebojša Ž. |
| المصدر: | Science of Sintering, Vol 48, Iss 3, Pp 333-341 (2016) |
| بيانات النشر: | International Institute for the Science of Sintering, Beograd, 2016. |
| سنة النشر: | 2016 |
| المجموعة: | LCC:Chemical technology |
| مصطلحات موضوعية: | CaF2, Raman spectroscopy, IR spectroscopy, photoluminescence, Chemical technology, TP1-1185 |
| الوصف: | It must be noted that the main objective of this study was to obtain single crystals of calcium fluoride - CaF2, and after that the crystals were characterized with various spectroscopic methods. The crystals were grown using the Bridgman technique. By optimizing growth conditions, oriented CaF2 crystals up to 20 mm in diameter were grown. Number of dislocations in CaF2 crystals was 5×104 - 2×105 per cm2. Selected CaF2 single crystal is cut into several tiles with the diamond saw. The plates were polished, first with the silicon carbide, then the paraffin oil, and finally with a diamond paste. The obtained crystal wаs studied by Raman and infrared -IR spectroscopy. The crystal structure is confirmed by X-ray diffraction (XRD). One Raman and two IR optical modes predicted by group theory are observed. A low photoluminescence testifies that the concentration of oxygen defects within the host CaF2 is small. All performed investigations show that the obtained CaF2 single crystal has good optical quality, which was the goal of this work. [Projekat Ministarstva nauke Republike Srbije, br. III 45003 i br. TR34011] |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | English |
| تدمد: | 0350-820X 1820-7413 |
| Relation: | https://doaj.org/toc/0350-820X; https://doaj.org/toc/1820-7413 |
| DOI: | 10.2298/SOS1603333E |
| URL الوصول: | https://doaj.org/article/4495032e0ff34f858e088b81055a162f |
| رقم الانضمام: | edsdoj.4495032e0ff34f858e088b81055a162f |
| قاعدة البيانات: | Directory of Open Access Journals |
Full Text Finder | تدمد: | 0350820X 18207413 |
|---|---|
| DOI: | 10.2298/SOS1603333E |