Influence of Annealing Process on Soft Magnetic Properties of Fe-B-C-Si-P Amorphous Alloys
| العنوان: | Influence of Annealing Process on Soft Magnetic Properties of Fe-B-C-Si-P Amorphous Alloys |
|---|---|
| المؤلفون: | Jili Jia, You Wu, Lingxiang Shi, Ranbin Wang, Wenhui Guo, Hengtong Bu, Yang Shao, Na Chen, Kefu Yao |
| المصدر: | Materials, Vol 17, Iss 6, p 1447 (2024) |
| بيانات النشر: | MDPI AG |
| سنة النشر: | 2024 |
| المجموعة: | Directory of Open Access Journals: DOAJ Articles |
| مصطلحات موضوعية: | amorphous alloy, long-time annealing, soft magnetic properties, magnetic domain, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
| الوصف: | It is well known that the annealing process plays a key role in tuning the properties of Fe-based amorphous soft magnetic alloys. However, the optimal annealing process for a particular amorphous alloy is often difficult to determine. Here, Fe 81.4 B 13.2 C 2.8 Si 1.8 P 0.8 and Fe 82.2 B 12.4 C 2.8 Si 1.8 P 0.8 amorphous alloys (denoted as Fe 81.4 and Fe 82.2 ) were prepared to systematically study the effects of the annealing temperature and time on the soft magnetic properties. The results show that the optimum annealing temperature ranges of the Fe 81.4 and Fe 82.2 amorphous alloys were 623 K to 653 K and 593 K to 623 K, and their coercivity ( H c ) values were only 2.0–2.5 A/m and 1.3–2.7 A/m, respectively. Furthermore, a characteristic temperature T ai was obtained to guide the choosing of the annealing temperature at which the dB s / dT begins to decrease rapidly. Based on the theory of spontaneous magnetization, the relationship between T ai and the optimum annealing temperature ranges was analyzed. When the annealing temperature was higher than T ai , the effect of the internal magnetic field generated by spontaneous magnetization on the relaxation behavior was significantly reduced, and the alloys exhibited excellent soft magnetic properties. It is worth indicating that when annealed at 603 K (slightly higher than T ai ), the Fe 82.2 amorphous alloys exhibited excellent and stable soft magnetic properties even if annealed for a long time. The H c of Fe 82.2 B 12.4 C 2.8 Si 1.8 P 0.8 amorphous alloys was only 1.9 A/m when annealed at 603 K for 330 min. This value of T ai is expected to provide a suggestion for the proper annealing temperature of other amorphous soft magnetic alloys. |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| تدمد: | 1996-1944 |
| Relation: | https://www.mdpi.com/1996-1944/17/6/1447; https://doaj.org/toc/1996-1944; https://doaj.org/article/5263348564a14cd49f4140aec65ed9e1 |
| DOI: | 10.3390/ma17061447 |
| الاتاحة: | https://doi.org/10.3390/ma17061447 https://doaj.org/article/5263348564a14cd49f4140aec65ed9e1 |
| رقم الانضمام: | edsbas.C0344D09 |
| قاعدة البيانات: | BASE |
Full Text Finder | تدمد: | 19961944 |
|---|---|
| DOI: | 10.3390/ma17061447 |