Synthesis and Characterization of High Conductivity Polyaniline Prepared at Room Temperature
| العنوان: | Synthesis and Characterization of High Conductivity Polyaniline Prepared at Room Temperature |
|---|---|
| المؤلفون: | Budi, Setia, Puspa Rini, Eka, Paristiowati, Maria, Imaduddin, Agung, Syafei, Devi |
| المصدر: | Chemistry and Materials; Vol. 1 No. 1 (2022); 7-11 ; 2828-2310 ; 2828-271X ; 10.56425/cma.v1i1 |
| بيانات النشر: | Pusat Inovasi Sains |
| سنة النشر: | 2022 |
| مصطلحات موضوعية: | High conductivity, Polyaniline, Oxidative polimerization |
| الوصف: | In this study, polyaniline was successfully synthesized using an oxidative polymerization method at room temperature. The polymerizations were carried out with and without stirring process under ultraviolet (UV) irradiation. The polyaniline was characterized by FTIR, XRD, SEM, SAA, and Four Point Probe. It is found that UV irradiation and stirring could increase the surface area and conductivity of polyaniline. The surface area obtained for stirred and unstirred polymerization were 37.9 m2/g and 29.0 m2/g, respectively. Moreover, conductivity values for stirred and unstirred polymerization were found as 1.22 S/cm and 1.08 S/cm respectively. This result shows that polyaniline synthesized by stirring treatment obtained uniform morphology, smaller size, greater crystallinity, higher BET surface area, and higher conductivity than that that of without stirring. |
| نوع الوثيقة: | article in journal/newspaper |
| وصف الملف: | application/pdf |
| اللغة: | English |
| Relation: | https://journal.piscience.org/cma/article/view/21/10; https://journal.piscience.org/cma/article/view/21 |
| DOI: | 10.56425/cma.v1i1.21 |
| الاتاحة: | https://journal.piscience.org/cma/article/view/21 https://doi.org/10.56425/cma.v1i1.21 |
| Rights: | Copyright (c) 2022 Authors ; https://creativecommons.org/licenses/by/4.0 |
| رقم الانضمام: | edsbas.998074E5 |
| قاعدة البيانات: | BASE |
| DOI: | 10.56425/cma.v1i1.21 |
|---|