Performance of aerated lightweighted concrete using aluminum lathe and pumice under elevated temperature
| العنوان: | Performance of aerated lightweighted concrete using aluminum lathe and pumice under elevated temperature |
|---|---|
| المؤلفون: | Çelik, Ali İhsan, Özdöner, Nebi, Karalar, Memduh, Özkılıç, Yasin Onuralp |
| سنة النشر: | 2024 |
| الوصف: | The primary objective of this study is to investigate the production and performance characteristics of structuralconcrete incorporating varying proportions (0%, 25%, and 50% by volume) of pumice stone, as well as aluminum lathe as anadditive at 0%, 1%, 2%, and 3%, under fire conditions. The experiment will be conducted over a period of up to 1 hour, attemperatures ranging from 24°C, 200°C, 400°C and 600°C. For the purpose of this, a total of twelve test samples weremanufactured, and then tests of compressive strength (CS), splitting tensile strength (STS), and flexural strength (FS) wereperformed on these samples.Next, a comparison was made between the obtained values and the influence of temperature. Toachieve this objective, the manufactured samples were placed at temperatures of 200°C, 400°C, and 600°C for a duration of 1hour, and were subjected to the influence of temperature.These values at 24 °C were then contrasted with the CS results obtainedfrom test samples that were subjected to the temperature effect for an hour at 200 °C, 400 °C, and 600 °C. A comprehensiveanalysis of the test outcomes reveals that the incorporation of aluminum lathe wastes into a mixture results in a significantreduction in the compressive strength of the concrete. As a result of this adjustment, the CS values dropped by 32.93%, 45.70%,and 52.07%, respectively. Furthermore, It was shown that testing the ratios of pumice stone alone resulted in a decrease in CSoutcomes. Additionally, it was found that the presence of higher temperatures is clearly the primary factor contributing to thedecrease in the strength of concrete. Due to elevated temperatures, the CS values decreased by 19.88%, 28.27%, and 38.61%respectively.After this investigation, an equation that explains the connection between CS and STS was provided through theutilization of the data of the experiments that were carried out |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| Relation: | c2aad02e-5cc3-42bb-884b-1ee9649bf328; https://avesis.kayseri.edu.tr/publication/details/c2aad02e-5cc3-42bb-884b-1ee9649bf328/oai |
| DOI: | 10.12989/scs.2024.51.3.271 |
| الاتاحة: | https://doi.org/10.12989/scs.2024.51.3.271 https://avesis.kayseri.edu.tr/publication/details/c2aad02e-5cc3-42bb-884b-1ee9649bf328/oai |
| Rights: | info:eu-repo/semantics/openAccess |
| رقم الانضمام: | edsbas.95164592 |
| قاعدة البيانات: | BASE |
| DOI: | 10.12989/scs.2024.51.3.271 |
|---|