The electrical characteristic of an MIS structure with biocompatible minerals doped (Brushite+Monetite: PVC) interface layer
| العنوان: | The electrical characteristic of an MIS structure with biocompatible minerals doped (Brushite+Monetite: PVC) interface layer |
|---|---|
| المؤلفون: | Altındal, Ş., Ulusoy, Murat, Mirzaei-Kalar, Zeinab, Özçelik, Süleyman, Azizian-Kalandaragh, Y. |
| سنة النشر: | 2022 |
| الوصف: | © 2022 Elsevier B.V.In this research work, by using biocompatible minerals as an additive, the electrical response of the structure was measured, and its convenience in passivating Nss was examined. The I-V and C(G)-V-f measurements were executed with wide range voltages (from −3 V to +4 V (0.05 V steps)) and frequencies (from 2 kHz to 2 MHz) at room temperature. When the Ri-V curves were examined, significant increases were observed in the depletion region. Additionally, the Rs value was obtained as approximately 380 Ω at 2 MHz from C-V measurements. Main parameters such as n, I0, ϕB0, Rs and RR obtained from I-V measurements are 2.46, 1.28×10−9 A, 0.822 eV, 1.56 kΩ, and 1.5×105, respectively. The fluctuations of Nss depending on both voltage and energy distribution were investigated with three different methods. The Nss average value obtained from the I-V measurement is approximately 2.8×1013 eV−1.cm2. From the Chf-Clf method, the average Nss value is approximately 1.33×1012 eV−1.cm−2. Finally, from the conductance method, the Nss and τ values vary from 2.30×1011 eV−1.cm−2 to 1.16×1012 eV−1.cm−2, and from 1.37×10−5 s to 5.25×10−5 s, respectively. With this method, the average Nss value was calculated as 8×1011 eV−1.cm−2. |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| Relation: | eeaf5d8d-d3b7-4d10-a6f5-f7fdb0965989; https://avesis.gazi.edu.tr/publication/details/eeaf5d8d-d3b7-4d10-a6f5-f7fdb0965989/oai |
| DOI: | 10.1016/j.mee.2022.111768 |
| الاتاحة: | https://doi.org/10.1016/j.mee.2022.111768 https://avesis.gazi.edu.tr/publication/details/eeaf5d8d-d3b7-4d10-a6f5-f7fdb0965989/oai |
| Rights: | info:eu-repo/semantics/closedAccess |
| رقم الانضمام: | edsbas.89A77FB |
| قاعدة البيانات: | BASE |
| DOI: | 10.1016/j.mee.2022.111768 |
|---|