Li Chemical and Tracer Diffusivities in LiCoO 2 Sintered Pellets
| العنوان: | Li Chemical and Tracer Diffusivities in LiCoO 2 Sintered Pellets |
|---|---|
| المؤلفون: | Erwin Hüger, Harald Schmidt |
| المصدر: | Batteries, Vol 10, Iss 12, p 446 (2024) |
| بيانات النشر: | MDPI AG |
| سنة النشر: | 2024 |
| المجموعة: | Directory of Open Access Journals: DOAJ Articles |
| مصطلحات موضوعية: | LiCoO 2, diffusion, thermodynamic factor, EIS, PITT, SIMS, Production of electric energy or power. Powerplants. Central stations, TK1001-1841, Industrial electrochemistry, TP250-261 |
| الوصف: | LiCoO 2 (LCO) is a crucial active material for positive electrodes of commercial lithium-ion batteries. It is typically present in the form of micrometer-sized LCO particles, which are surrounded by binders and conductive agents with a thickness of tens of microns. In order to determine the intrinsic Li transport parameters of pure crystalline LCO, it is necessary to measure the Li diffusivity at room temperature in sintered LCO pellets free of additives. The LCO sintered bulk material consists of interconnected, about 3 µm clusters, composed of grains of about 70 nanometers in size. The Li chemical and tracer diffusivities are determined using electrochemical impedance spectroscopy (EIS) and potentiostatic intermittent titration technique (PITT), while the latter ones are in the range between 10 −9 and 10 −28 m 2 s −1 , depending on the application of different relevant formulas and characteristic parameters. Consequently, it is essential to apply a classical non-electrochemical and Li selective method of tracer diffusion determination like 6 Li depth profiling and secondary ion mass spectrometry (SIMS) for comparison. Li tracer diffusivities of about 10 −22 m 2 s −1 at room temperature are obtained by the extrapolation of the SIMS results from higher temperatures. This significantly narrows the range of reliable electrochemically determined Li tracer diffusivities to a more limited range, between 10 −21 and 10 −22 m 2 s −1 . |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| Relation: | https://www.mdpi.com/2313-0105/10/12/446; https://doaj.org/toc/2313-0105; https://doaj.org/article/5ea59cdb5df84f8a8102fab4c1bd75ea |
| DOI: | 10.3390/batteries10120446 |
| الاتاحة: | https://doi.org/10.3390/batteries10120446 https://doaj.org/article/5ea59cdb5df84f8a8102fab4c1bd75ea |
| رقم الانضمام: | edsbas.78DC9EA5 |
| قاعدة البيانات: | BASE |
| DOI: | 10.3390/batteries10120446 |
|---|