Anionic ring-opening copolymerization of styrene oxide with monosubstituted oxiranes: analysis of composition of prepared new copolyether-diols by MALDI-TOF mass spectrometry
| العنوان: | Anionic ring-opening copolymerization of styrene oxide with monosubstituted oxiranes: analysis of composition of prepared new copolyether-diols by MALDI-TOF mass spectrometry |
|---|---|
| المؤلفون: | Grobelny, Zbigniew, Jurek-Suliga, Justyna, Golba, Sylwia, Matlengiewicz, Marek |
| سنة النشر: | 2019 |
| المجموعة: | The Repository of the University of Silesia (RE-BUŚ) / Repozytorium Uniwersytetu Śląskiego |
| مصطلحات موضوعية: | Copolyether-diols, Anionic ring-opening copolymerization, Styrene oxide, MALDI-TOF |
| الوصف: | Several new random copolyethers of styrene oxide (SO) and other monosubstituted oxirane as comonomer, i.e., propylene oxide (PO), isopropyl glycidyl ether (IPGE) or allyl glycidyl ether (AGE), were synthesized in THF solution at room temperature. As initiator monopotassium salt of dipropylene glycol activated by 18-crown-6 complexing agent was used. Synthesized copolyether-diols were characterized by SEC, 13C NMR and MALDI-TOF techniques. They were unimodal and had Mn = 3500–4600 and relatively low dispersity (Mw/Mn = 1.16–1.18). Low unsaturation of the products resulted from chain transfer reaction to styrene oxide. Composition of SO/PO-diol, SO/IPGE-diol and SO/AGE-diol copolymers was determined by MALDI-TOF mass spectrometry. Homopolymers were not formed during the processes. |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| تدمد: | 0170-0839 1436-2449 |
| Relation: | "Polymer Bulletin (Berl., Print)" (2019) (online first); http://hdl.handle.net/20.500.12128/11282 |
| DOI: | 10.1007/s00289-019-02717-y |
| الاتاحة: | https://hdl.handle.net/20.500.12128/11282 https://doi.org/10.1007/s00289-019-02717-y |
| Rights: | Uznanie autorstwa 3.0 Polska ; http://creativecommons.org/licenses/by/3.0/pl/ |
| رقم الانضمام: | edsbas.4732093E |
| قاعدة البيانات: | BASE |
| تدمد: | 01700839 14362449 |
|---|---|
| DOI: | 10.1007/s00289-019-02717-y |