التفاصيل البيبلوغرافية
| العنوان: |
Technology, Preparation and Properties of the Cast Glass-Coated Magnetic Microwires |
| المؤلفون: |
Serghei Baranov, Vladimir Larin, Alexander Torcunov |
| المصدر: |
Crystals; Volume 7; Issue 6; Pages: 136 |
| بيانات النشر: |
Multidisciplinary Digital Publishing Institute |
| سنة النشر: |
2017 |
| المجموعة: |
MDPI Open Access Publishing |
| مصطلحات موضوعية: |
glass-coated magnetic microwires, Taylor–Ulitovsky method, dynamical viscosity, casting rate, cooling rate, coercive field |
| الوصف: |
Magnetic properties of cast amorphous and nanocrystalline microwires have been reviewed considering their potential application. Microwires were produced from Co Fe Mn Cr Cu B and Si using the Taylor–Ulitovsky method. Technological aspects of the Taylor–Ulitovsky method for fabrication of glass-coated microwire with different structure are analyzed. Magnetic microwires demonstrate a large variety of magnetic behaviors, which is important for sensing applications. Depending on the chemical composition of the metallic core, for Co-, Fe- and Ni-based composition, the microwires’ properties are very different. The geometrical characteristics (diameter of metallic core and thickness of the glass) of the microwire depend on the physical properties of a metallic composition and of glass and the parameters of the heating inductor and the speed of obtaining a microwire. The diameter of metallic core in these microwires can range from 0.5 to 70 μm, and their thickness of the glass can vary from 1 to 50 μm. |
| نوع الوثيقة: |
text |
| وصف الملف: |
application/pdf |
| اللغة: |
English |
| Relation: |
Inorganic Crystalline Materials; https://dx.doi.org/10.3390/cryst7060136 |
| DOI: |
10.3390/cryst7060136 |
| الاتاحة: |
https://doi.org/10.3390/cryst7060136 |
| Rights: |
https://creativecommons.org/licenses/by/4.0/ |
| رقم الانضمام: |
edsbas.2CE2B22C |
| قاعدة البيانات: |
BASE |