Synthesis and Characterization of Biomorphic Ceo2 Obtained By Using Egg Shell Membrane as Template
| العنوان: | Synthesis and Characterization of Biomorphic Ceo2 Obtained By Using Egg Shell Membrane as Template |
|---|---|
| المؤلفون: | Biljana Babić, Jelena Gulicovski, Marija Prekajski, Jelena Pantić, Branko Matović, Miroslav Miljković, Dušan Bučevac |
| المصدر: | Processing and Application of Ceramics Processing and Application of Ceramics, Vol 8, Iss 2, Pp 81-85 (2014) |
| سنة النشر: | 2012 |
| مصطلحات موضوعية: | Materials science, XRD, Scanning electron microscope, microstructure, Oxide, Nanotechnology, bio-templating, law.invention, lcsh:TP785-869, chemistry.chemical_compound, Adsorption, law, Biomorphic materials, Calcination, BET, Microstructure, Egg shell membrane, Cerium nitrate, Membrane, Template, lcsh:Clay industries. Ceramics. Glass, chemistry, Chemical engineering, SEM, Ceramics and Composites, CeO2 |
| الوصف: | Porous CeO2 was obtained by bio-inspired route using egg shell membranes (ESM) as a template. ESM extracted from the fresh chicken eggs were washed with distilled water and immersed in solution of Ce(NO3)(3) x 6 H2O for seven days. Samples were subsequently thermally treated at temperature ranging from 600 to 1200 degrees C in argon and air.To study the crystallization process, samples were heated to temperature ranging from 600 to 1200 degrees C, in air, at different temperatures (600, 800, 1000 and 1200 degrees C). Samples were characterized by nitrogen adsorption measurements, X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD of samples revealed that well crystallized CeO2 is obtained even at temperature as low as 600 degrees C. SEM images confirmed that morphology of obtained CeO2 is a replica of the morphology of the original ESM. International Conference ModTech Proceedings, 16th International Conference on Modern Technologies, Quality and Innovation, May 24-26, 2012, Sinaia, Romania |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::a72abfb78c8e9aa69a20137c8ced5aab https://vinar.vin.bg.ac.rs/handle/123456789/7150 |
| Rights: | OPEN |
| رقم الانضمام: | edsair.doi.dedup.....a72abfb78c8e9aa69a20137c8ced5aab |
| قاعدة البيانات: | OpenAIRE |
| الوصف غير متاح. |