Structure and Properties of Ceramics Based on Monetite and Nanodispersed Silica
| العنوان: | Structure and Properties of Ceramics Based on Monetite and Nanodispersed Silica |
|---|---|
| المؤلفون: | Ya. I. Yevich, A. V. Kotlyarchuk, G. B. Tovstonog, O. Ye. Sych, S. O. Ostapenko, N. D. Pinchuk, V. V. Pasichnyi |
| المصدر: | Powder Metallurgy and Metal Ceramics. 54:175-182 |
| بيانات النشر: | Springer Science and Business Media LLC, 2015. |
| سنة النشر: | 2015 |
| مصطلحات موضوعية: | Materials science, Metals and Alloys, Mineralogy, Sintering, Calcium pyrophosphate, engineering.material, Condensed Matter Physics, Wollastonite, chemistry.chemical_compound, Compressive strength, chemistry, Chemical engineering, Mechanics of Materials, visual_art, Calcium silicate, Materials Chemistry, Ceramics and Composites, visual_art.visual_art_medium, engineering, Silicon carbide, Ceramic, Porosity |
| الوصف: | Calcium–phosphate ceramics based on monetite and nanosized silica are produced by sintering at 500°C. It is established that phase changes and solid-phase reactions occur during sintering to form ceramics that contain β-calcium pyrophosphate (Ca2P2O7), calcium silicate (wollastonite, CaSiO3), and insignificant amount of β-tricalcium phosphate (Ca3(PO4)2). It is shown that the addition of silica inhibits re-crystallization of calcium pyrophosphate into tricalcium phosphate, if compared with ceramics prepared from monetite with no silica added. It is established that increasing the silica content in the starting composition leads to a decrease in the minimum pore size from 0.83 to 0.21 μm. Highly pure nanosized silica (content of SiO2 > 99%) prepared by heat-treating of silicon carbide waste in a solar furnace is used in our research. The porosity of ceramics produced reaches 43.5–46.8% and the compressive strength is 16–24 MPa. |
| تدمد: | 1573-9066 1068-1302 |
| DOI: | 10.1007/s11106-015-9695-6 |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::af6808e53dae91167a11876428c51425 https://doi.org/10.1007/s11106-015-9695-6 |
| Rights: | CLOSED |
| رقم الانضمام: | edsair.doi...........af6808e53dae91167a11876428c51425 |
| قاعدة البيانات: | OpenAIRE |
| تدمد: | 15739066 10681302 |
|---|---|
| DOI: | 10.1007/s11106-015-9695-6 |