Pulse electrodeposition of aluminium coatings from molten salt bath; effect of processing parameters on the coatings' corrosion and wear behaviour. |
| المؤلفون: |
Arabnejad, Ali, Najafisayar, Pooria |
| المصدر: |
Transactions of the Institute of Metal Finishing; Nov2022, Vol. 100 Issue 6, p305-312, 8p |
| مصطلحات موضوعية: |
ALLOY plating, FRETTING corrosion, COATING processes, FUSED salts, COMPOSITE coating, SURFACE coatings, ALUMINUM, SCANNING electron microscopy |
| مستخلص: |
In this study, Al coatings were pulse electrodeposited from a molten salt electrolyte onto copper substrates. The effects of applied peak current density, pulse current frequency and duty cycle on the morphology, microstructure, corrosion behaviour and tribological properties of the coatings were investigated by scanning electron microscopy, X-ray diffraction, potentiodynamic polarisation, electrochemical impedance spectroscopy and pin-on-disc wear test methods. The results showed that the changes in processing parameters changed the morphological and microstructural features of the resulting coatings, which in turn affected their corrosion and wear behaviours. Coatings with smoother surfaces, finer crystallite size and more compact morphologies that were electrodeposited at higher applied peak current density (up to 80 mA cm−2), higher pulse current frequency (up to 50 Hz) and higher duty cycle (up to 50%) exhibited more corrosion and wear resistance than the others. [ABSTRACT FROM AUTHOR] |
|
Copyright of Transactions of the Institute of Metal Finishing is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |