التفاصيل البيبلوغرافية
| العنوان: |
BRAZING Q&A. |
| المؤلفون: |
KAY, DAN, SHAPIRO, ALEXANDER E., HIRTHE, TIM P. |
| المصدر: |
Welding Journal; Aug2022, Vol. 101 Issue 8, p24-26, 3p, 2 Color Photographs |
| مصطلحات موضوعية: |
BRAZING, BRAZING alloys, FILLER metal |
| مستخلص: |
Another attractive feature of the Ni-Cr alloy powder was that it had a low enough initial melting point (solidus) that might allow its use for joining jet engine metal components via furnace brazing. Q: Can you please share some of the history about high-temperature brazing filler metal (BFM) of jet engine turbine blades? Peaslee was searching for a high-temperature BFM to replace the silver-manganese alloy (85%Ag/15%Mn) that had been developed by the Germans during WWII and was the standard high-temperature BFM at that time. [Extracted from the article] |
|
Copyright of Welding Journal is the property of American Welding Society and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Supplemental Index |