| العنوان: |
The effect of Si doping on the electrical properties of B12As2 thin films on (0001) 6H-SiC substrates. |
| المؤلفون: |
Xu, Zhou, Edgar, J. H., Look, D. C., Baumann, S., Bleiler, R. J., Wang, S. H., Mohney, S. E. |
| المصدر: |
Journal of Applied Physics; 3/1/2007, Vol. 101 Issue 5, p053710-N.Pag, 5p, 3 Charts, 5 Graphs |
| مصطلحات موضوعية: |
THIN films, CHEMICAL vapor deposition, SECONDARY ion mass spectrometry, HYDROGEN, WIDE gap semiconductors, HALL effect, SURFACES (Technology) |
| مستخلص: |
The ability to control the resistivity of the wide band gap semiconductor B12As2 by doping with silicon was verified. The electrical properties of nominally undoped and Si-doped rhombohedral B12As2 thin films on semi-insulating 6H-SiC (0001) substrates prepared by chemical vapor deposition were subjected to Hall effect measurements. Varying the Si concentration in the B12As2 thin films from 7×1018 to 7×1021 at./cm3 (as measured by secondary ion mass spectrometry) decreased the resistivities of the p-type B12As2 films from 2×105 to 10 Ω cm. The resistivities of the B12As2 films were decreased by one to two orders of magnitude after rapid thermal annealing for 30 s in argon. The spatial distribution of the hydrogen concentration was measured before and after annealing. No changes were detected, casting doubt on hydrogen as being the cause for the change in the resistivities of the B12As2 films with annealing. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |