Be2B monolayer as a well-balanced performance anode for lithium-ion batteries with ultrahigh theoretical capacity and low diffusion barrier. |
| المؤلفون: |
Lu, Zheng, Liu, Chun-Sheng, Ye, Xiao-Juan |
| المصدر: |
Journal of Applied Physics; 12/14/2024, Vol. 136 Issue 22, p1-10, 10p |
| مصطلحات موضوعية: |
ENERGY storage, OPEN-circuit voltage, DIFFUSION barriers, TENSILE strength, LITHIUM-ion batteries, MONOMOLECULAR films |
| مستخلص: |
Lithium-ion batteries (LIBs) are the most crucial part of energy storage systems. The lower molar weight of anodes can achieve a higher theoretical capacity. We explore the performance of a Be2B monolayer as an anode for LIBs. By first-principles calculations, we reveal that the Be2B monolayer shows excellent tensile strength, which suggests that it can deal with the volume expansion during the adsorption process. Furthermore, the Be2B monolayer can stably adsorb Li atoms with an adsorption energy of −0.98 eV. Moreover, the Be2B monolayer exhibits a low diffusion barrier (0.066 eV), an ultra-high theoretical capacity (3717 mA h g−1), and a moderate open circuit voltage (0.59 V). We also confirm the wettability of the Be2B monolayer in common electrolytes and investigate the adsorption and diffusion properties of Li on Be2B/graphene heterostructure. The introduction of graphene enhances the migration behavior of Li, suggesting the fast charging/discharging capability. Based on the above-mentioned properties, we propose that the Be2B monolayer can act as a high-performance anode material. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |