التفاصيل البيبلوغرافية
| العنوان: |
Thermodynamic Simulation Calculations of Phase Transformations in Low-Aluminum Zn-Al-Mg Coatings. |
| المؤلفون: |
Zhang, Ziyue, Zhang, Jie, Zhao, Xingyuan, Cheng, Xuequn, Liu, Xin, Zhang, Qifu |
| المصدر: |
Materials (1996-1944); Jun2024, Vol. 17 Issue 11, p2719, 13p |
| مصطلحات موضوعية: |
PHASE transitions, SURFACE coatings, TERNARY system, X-ray diffraction, DATABASES, MAGNESIUM, ALUMINUM-zinc alloys |
| مستخلص: |
This study delves into the formation, transformation, and impact on coating performance of MgZn2 and Mg2Zn11 phases in low-aluminum Zn-Al-Mg alloy coatings, combining thermodynamic simulation calculations with experimental verification methods. A thermodynamic database for the Zn-Al-Mg ternary system was established using the CALPHAD method, and this alloy's non-equilibrium solidification process was simulated using the Scheil model to predict phase compositions under varying cooling rates and coating thicknesses. The simulation results suggest that the Mg2Zn11 phase might predominate in coatings under simulated production-line conditions. However, experimental results characterized using XRD phase analysis show that the MgZn2 phase is the main phase existing in actual coatings, highlighting the complexity of the non-equilibrium solidification process and the decisive effect of experimental conditions on the final phase composition. Further experiments confirmed that cooling rate and coating thickness significantly influence phase composition, with faster cooling and thinner coatings favoring the formation of the metastable phase MgZn2. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |