ON SOME FEATURES OF THE GRAIN AND SUBGRAIN SIZE IN A CU-CR-ZR ALLOY AFTER ECAP PROCESSING AND AGING. |
| المؤلفون: |
ABIB, K., ALILI, B., BAUDIN, T., HELBERT, A.-L., BRISSET, F., LITYNSKA-DOBRZYNSKA, L., ZIEBA, P., BRADAI, D. |
| المصدر: |
Archives of Metallurgy & Materials; 2024, Vol. 69 Issue 1, p9-16, 8p |
| مصطلحات موضوعية: |
GRAIN size, GRAIN, TRANSMISSION electron microscopy, ALLOYS, ESTIMATION theory, ELECTRON diffraction |
| مستخلص: |
A Cu-1Cr-0.1Zr alloy has been subjected to ECAP processing via route Bc and aging at 250-800°C. Electron BackScatter diffraction (EBSD), Transmission Electron Microscopy (TEM) and X-Ray Diffraction Line Profile Analysis (XRDLPA) techniques have been used to unveil some peculiarities of the grain and subgrain structure with a special emphasis on the comparison of the grain size estimated by the three techniques. For the alloy ECAP processed and aged up to 16 passes, the grain size (from EBSD, 0.2 < d < 5 µm), subgrain size (from TEM, d ~ 0.75 µm) and "apparent" average crystallite size (from XRDLPA, d < 0.25 µm) are manifestly different. The results were compared to the published data and analyzed based on the fundamental aspects of these techniques. [ABSTRACT FROM AUTHOR] |
|
Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |