A New Design for Magnetic Poly(vinyl pivalate) for Biomedical Applications: Synthesis, Characterization, and Evaluation of Cytotoxicity in Fibroblasts, Keratinocytes, and Human Melanoma Cells. |
| المؤلفون: |
Araujo, Robson T., Neta, Maria S. B., Coaquira, José A. H., Chaves, Sacha B., Machado, Fabricio |
| المصدر: |
Colloids & Interfaces; Mar2022, Vol. 6 Issue 1, p7-7, 23p |
| مصطلحات موضوعية: |
FEVER, THERMOPLASTIC composites, X-ray diffractometers, METHACRYLIC acid, NANOCOMPOSITE materials |
| مستخلص: |
Polymers containing magnetic properties play an important role in biomedical therapies, such as embolotherapy or hyperthermia, for their differentiated properties. In this work, magnetite (Fe3O4) nanoparticles were synthesized by the coprecipitation method and dispersed into a thermoplastic matrix of poly(vinyl pivalate) through an emulsion polymerization process. The main goal was the individual encapsulation of magnetite nanoparticles to improve the magnetic response of the magneto-polymeric materials using polymerizable carboxylic acids as coating agents, minimizing the leaching of nanoparticles throughout the nanocomposite formation. For this purpose, synthesized magnetite had its surface modified by acrylic acid or methacrylic acid to improve its individual encapsulation during the polymerization step, thus generating a series of magnetic nanocomposite materials containing different amounts of magnetite intended for biomedical applications. X-ray diffractometry and TEM measurements provided a mean size of approximately 8 nm for the pure magnetite nanoparticles and a spherical morphology. Acid-functionalized Fe3O4 had a size of approximately 6 nm, while the nanocomposites showed a size of approximately 7 nm. Magnetization measurement provided a saturation magnetization value of approximately 75 emu/g and confirmed superparamagnetic behavior at room temperature. DSC analysis showed a glass transition temperature of 65 °C for poly(vinyl pivalate)-based nanocomposites. The tests realized with homopolymer and magnetic composites against different cell lineages (i.e., fibroblasts, keratinocytes, and human melanoma) to evaluate the levels of cytotoxicity showed good results in the different exposure times and concentrations used, since the obtained results showed cell viability greater than 70% compared to the control group, suggesting that the synthesized materials are very promising for medical applications. [ABSTRACT FROM AUTHOR] |
|
Copyright of Colloids & Interfaces is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |