Mechanism of Action of the Tungsten Dopant in LiNiO2 Positive Electrode Materials. |
| المؤلفون: |
Geng, Chenxi, Rathore, Divya, Heino, Dylan, Zhang, Ning, Hamam, Ines, Zaker, Nafiseh, Botton, Gianluigi A., Omessi, Roee, Phattharasupakun, Nutthaphon, Bond, Toby, Yang, Chongyin, Dahn, J. R. |
| المصدر: |
Advanced Energy Materials; 2/10/2022, Vol. 12 Issue 6, p1-8, 8p |
| مصطلحات موضوعية: |
CATHODES, TRANSITION metal oxides, SCANNING electron microscopy, ELECTRODES, HEAT treatment, CRYSTAL grain boundaries, ELECTRON microscopy, TUNGSTEN |
| مستخلص: |
The addition of tungsten has been reported to greatly improve the capacity retention of Ni‐rich layered oxide cathode materials in lithium‐ion batteries. In this work, Ni(OH)2 precursors, coated with WO3 and also W‐containing precursors prepared by co‐precipitation followed by heat treatment with LiOH·H2O, are studied. Structural analysi s and electron microscopy show that W is incorporated as amorphous LixWyOz phases concentrated in all the grain boundaries between the primary particles of LiNiO2 (LNO) and on the surface of the secondary particles. Tungsten does not substitute for Ni or Li in the LNO lattice no matter how W is added at the precursor synthesis stage. Scanning electron microscopy (SEM) images show that adding W greatly suppresses primary particle growth during synthesis. In agreement with previous literature reports, cycling test results show that 1% W added to LNO can greatly improve charge–discharge capacity retention while also delivering a high specific capacity. The LixWyOz amorphous phases act as coating layer on both the primary and secondary particles, restrict primary particle growth during synthesis and increase the resistance of the secondary particles to microcracking. [ABSTRACT FROM AUTHOR] |
|
Copyright of Advanced Energy Materials is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |