Conductivity, microstructure and mechanical properties of tape-cast LATP with LiF and SiO2 additives. |
| المؤلفون: |
Gross, Jürgen Peter, Malzbender, Jürgen, Dashjav, Enkhtsetseg, Tietz, Frank, Schwaiger, Ruth |
| المصدر: |
Journal of Materials Science; Jan2022, Vol. 57 Issue 2, p925-938, 14p, 4 Black and White Photographs, 1 Diagram, 3 Charts, 3 Graphs |
| مصطلحات موضوعية: |
RIETVELD refinement, MICROSTRUCTURE, LITHIUM fluoride, IONIC conductivity, SOLID electrolytes, POLYELECTROLYTES, SUPERIONIC conductors |
| مستخلص: |
LATP sheets with LiF and SiO2 addition prepared by tape cast as electrolytes for solid-state batteries were characterized regarding conductivity, microstructure and mechanical properties aiming toward an optimized composition. The use of additives permitted a reduction of the sintering temperature. Rietveld analyses of the samples with additives revealed a phase mixture of NaSICON modifications crystallizing with rhombohedral and orthorhombic symmetry as a superstructure with space group Pbca. It seems that LiF acts as a sintering additive but also as a mineralizer for the superstructure of LATP. As general trend, higher LiF to SiO2 ratios led to lower porosities and higher values of elastic modulus and hardness determined by indentation testing, but the presence of the orthorhombic LATP leads to a decrease in the ionic conductivity. Micro-pillar testing was used to assess the crack growth behavior revealing weak grain boundaries. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Science is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |