التفاصيل البيبلوغرافية
| العنوان: |
Repair Bond Strength and Leakage of Non-Aged and Aged Bulk-fill Composite. |
| المؤلفون: |
Aquino, Cintia, Mathias, Caroline, Chasse Barreto, Suelem, Nóbrega Cavalcanti, Andrea, Maria Marchi, Giselle, Mathias, Paula, Barreto, Suelem Chasse, Cavalcanti, Andrea Nóbrega, Marchi, Giselle Maria |
| المصدر: |
Oral Health & Preventive Dentistry; 2020, Vol. 18 Issue 4, p783-791, 9p |
| مصطلحات موضوعية: |
BOND strengths, LEAKAGE, TUKEY'S test, SURFACE preparation, DENTAL bonding, DENTAL resins, TENSILE strength, MATERIALS testing, SURFACE properties, SILICON compounds |
| مستخلص: |
Purpose: This study evaluated repair protocols of a non-aged and aged bulk-fill composite in terms of bond strength and leakage.Materials and Methods: Ninety-six bulk-fill resin specimens were constructed; half were submitted to thermocycling. Specimens were divided into six groups (n = 16) according to the repair treatments: CG: no repair (control group); Ad: adhesive; DbAd: abrasion with diamond bur + adhesive; SbAd: sandblasting + adhesive; DbSiAd: abrasion with diamond bur + silane + adhesive; and SbSiAd: sandblasting + silane + adhesive. Resin blocks were bonded to the treated surfaces to simulate repair, and the specimens were submitted to microtensile bond strength testing. The failure area was evaluated under a stereomicroscope (40X magnification), and leakage after specimen immersion in silver nitrate solution for 24 h was evaluated under a microscope (200X magnification). Three-way ANOVA (surface treatment, chemical agent, aging) and Tukey's test were performed.Results: Ad and DbAd groups showed the lowest bond strengths, while Ad was the only group negatively influenced by aging. The other groups were statistically similar to the CG in both conditions. All groups exhibited leakage, but groups without silane presented a greater percentage of leakage, mainly when diamond burs were used. Thermocycling did not influence leakage, nor did surface treatment in groups with silane.Conclusion: For composite repair, the use of silane is recommended, mainly when diamond burs are used as a mechanical surface treatment. [ABSTRACT FROM AUTHOR] |
|
Copyright of Oral Health & Preventive Dentistry is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |