Tayloring PS/PCL blends: characteristics of processing and properties. |
| المؤلفون: |
de Souza Morais, Dayanne Diniz, França, Danyelle Campos, Araújo, Edcleide Maria, de Carvalho, Laura Hécker, Wellen, Renate Maria Ramos, de Oliveira, Amanda Dantas, de Melo, Tomás Jeferson Alves |
| المصدر: |
REM - International Engineering Journal; Jan-Mar2019, Vol. 72 Issue 1, p87-95, 9p |
| مستخلص: |
Blends of Polystyrene (PS) and Poly(e-caprolactone) (PCL) were twin screw extruded, two PSs, with low and high melt flow rate (MFR) were used and their feasibility within PCL investigated by means of torque rheometry, mechanical tests, heat deflection temperature (HDT) and scanning electron microscopy (SEM); predictive models were utilized to evaluate interfacial adhesion in PS/PCL blends. Results show that no decreasing was verified in torque rheometry plots suggesting thermally stable blends; elastic modulus decreased and elongation at break increased in PS/PCL blends compared to neat PS. PS/PCL blends with low MFR PS and higher PCL amount are more thermodynamically stable. Higher HDT was verified in PS/PCL blends. The trends observed applying predictive models are indicative of poor adhesion between PCL and PS, agreeing with coalescence and phase segregation as verified in SEM images. PS/PCL systems with higher MFR PS presented the best results. [ABSTRACT FROM AUTHOR] |
|
Copyright of REM - International Engineering Journal is the property of Rem: Escola de Minas and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |