Preparation of soft composite reinforced with auxetic warp-knitted spacer fabric for stab resistance. |
| المؤلفون: |
Xu, Wanli, Sun, Yaxin, Lin, Haitao, Wei, Chunyan, Ma, Pibo, Xia, Fenglin |
| المصدر: |
Textile Research Journal; Feb2020, Vol. 90 Issue 3/4, p323-332, 10p |
| مصطلحات موضوعية: |
SILICONE rubber, POISSON'S ratio, MATERIALS testing, PEAK load |
| مستخلص: |
Auxetic warp-knitted spacer fabrics have gained increasing interest due to their excellent properties, such as shear resistance, indentation resistance, synclastic curvature and so on. Soft composites made from auxetic warp-knitted spacer fabrics and A/B two-component silicone rubbers were studied in this paper. The stabbing resistance of composites made by different auxetic fabrics (Fabrics 1–4#) and at different filling rates (0%, 20%, 40%, 70%, 100%), respectively, were tested using a universal Material Testing System. The results show that the peak load, energy absorption and deformation displacement of the composites increase with an increase of auxetic performance and filling rate. In addition, a better auxetic effect and larger filling rate can result in less damage. The composites with a higher filling rate are more like an elastomer. The auxetic effect also has an important role in stabbing resistance, which is due to fabrics with a larger negative Poisson's ratio value having a denser face layer structure and more deformable units, which can lead to better stabbing resistance for the composites. [ABSTRACT FROM AUTHOR] |
|
Copyright of Textile Research Journal is the property of Sage Publications, Ltd. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |