REGULATIONS OF THE FORMATION OF BAINETIC COMPONENT MATRIX IN ECONOMY ALLOYED CHROMO-MANGANESE ALLOYS ; ЗАКОНОМІРНОСТІ ФОРМУВАННЯ БЕЙНІТНОЇ СКЛАДОВОЇ МАТРИЦІ В ЕКОНОМЛЕГОВАНИХ ХРОМОМАРГАНЦЕВИХ СПЛАВАХ
| العنوان: | REGULATIONS OF THE FORMATION OF BAINETIC COMPONENT MATRIX IN ECONOMY ALLOYED CHROMO-MANGANESE ALLOYS ; ЗАКОНОМІРНОСТІ ФОРМУВАННЯ БЕЙНІТНОЇ СКЛАДОВОЇ МАТРИЦІ В ЕКОНОМЛЕГОВАНИХ ХРОМОМАРГАНЦЕВИХ СПЛАВАХ |
|---|---|
| المؤلفون: | POHREBNA , N.E., NOSKO , O.A., AIUPOVA , T.A., HREBENIEVA , А.V., AIUPOV , O.A. |
| المصدر: | Physical Metallurgy and Heat Treatment of Metals; No. 1 (100) (2023): Metal Science and Heat Treatment of Metals; 73-78 ; Металловедение и термическая обработка металлов; № 1 (100) (2023): Metal Science and Heat Treatment of Metals; 73-78 ; Металознавство та термічна обробка металів; № 1 (100) (2023): Металознавство та термічна обробка металів; 73-78 ; 2413-7405 |
| بيانات النشر: | SHEI "Prydniprovska State Academy of Civil Engineering and Architecture" |
| سنة النشر: | 2023 |
| مصطلحات موضوعية: | хромомарганцевий чавун, бейніт, ізотермічна витримка, мікротвердість, твердість, chromium-manganese cast iron, isothermal soaking, microhardness, hardness |
| الوصف: | Purpose. The purpose of the investigation is to establish the regularities of the kinetics of supercooled austenite decomposition in the bainite temperature range (400−200 °C) in chromium-manganese cast iron for the development of thermal hardening regimes that increase the service life of products. Methodology. The object of the study are samples of research and industrial smelting of chrome-manganese cast iron containing 3,1 % carbon, 13,1 % chromium, and 15,75 % manganese. The study of the supercooled austenite decomposition kinetics was carried out by the dilatometric method in the temperature range of 400−200 °C, the study of the microstructure, phase composition, as well as the measurement of microhardness and hardness was carried out according to standard methods. Scientific novelty. The peculiarities of the supercooled austenite decomposition kinetics in the bainite temperature range (400−200 °С) in chromium-manganese cast iron were determined, the structure of the cast iron after aging consists of eutectic carbides Me (Cr, Mn, Fe)7C3, products of austenite decomposition, secondary carbides Me (Cr, Mn, Fe)7C3, Me (Cr, Mn, Fe)3C, as well as untransformed austenite in the amount of 70.75 %. The maximum hardness of the experimental cast iron was established during isothermal exposure at 350 °C for 35 hours. Practical value. The established regularities of the chromium-manganese cast iron structure formation and the determined and optimized temperature-time intervals of the supercooled austenite isothermal decomposition in cast iron are the basis for the development of heat treatment regimes to increase the strength, wear resistance of the material and the service life of its products. ; Мета роботи − встановлення закономірностей кінетики розпаду переохолодженого аустеніту в бейнітній області температур (400−200 °С) у хромомарганцевому чавуні для розроблення режимів термічного зміцнення, що підвищують термін служби виробів. Методика. Об'єктом дослідження служили зразки дослідно-промислової плавки ... |
| نوع الوثيقة: | article in journal/newspaper |
| وصف الملف: | application/pdf |
| اللغة: | English |
| Relation: | http://mtom.pgasa.dp.ua/article/view/280451/274758; http://mtom.pgasa.dp.ua/article/view/280451 |
| DOI: | 10.30838/J.PMHTM.2413.280323.73.947 |
| الاتاحة: | http://mtom.pgasa.dp.ua/article/view/280451 https://doi.org/10.30838/J.PMHTM.2413.280323.73.947 |
| Rights: | Copyright (c) 2023 Pohrebna N.E., Nosko O.A., Aiupova T.A., Hrebenieva А.V., Aiupov O.A. |
| رقم الانضمام: | edsbas.EEFB018D |
| قاعدة البيانات: | BASE |
| DOI: | 10.30838/J.PMHTM.2413.280323.73.947 |
|---|