Microstructural Evolution after Cold Forming and Recrystallization Annealing in Commercially Pure Titanium Sheet
| العنوان: | Microstructural Evolution after Cold Forming and Recrystallization Annealing in Commercially Pure Titanium Sheet |
|---|---|
| المؤلفون: | Wei Lv, Shao Pu Kang, Jin Yu Li, Zhuang Li, Huan Huan Yu |
| المصدر: | Materials Science Forum. 896:193-197 |
| بيانات النشر: | Trans Tech Publications, Ltd., 2017. |
| سنة النشر: | 2017 |
| مصطلحات موضوعية: | 010302 applied physics, Equiaxed crystals, Microstructural evolution, Materials science, Annealing (metallurgy), Mechanical Engineering, Metallurgy, Recrystallization (metallurgy), chemistry.chemical_element, 02 engineering and technology, 021001 nanoscience & nanotechnology, Condensed Matter Physics, 01 natural sciences, Indentation hardness, Hot working, chemistry, Mechanics of Materials, 0103 physical sciences, Dynamic recrystallization, General Materials Science, 0210 nano-technology, Titanium |
| الوصف: | Different cold rolling and recrystallization annealing of commercially pure titanium (CP-Ti) sheet was conducted. Microstructural evolution in commercially pure titanium sheet after cold forming and recrystallization annealing were investigated. Cold forming properties using a microstructural analysis, Vickers microhardness and erichsen value measurements were performed. Alpha grain sizes of processing 1 and 2 are 38.67μm and 40.12μm, respectively. Erichsen values of the specimens of processing 2 reaches the high value. This is attributed to recrystallization annealing. Equiaxed alpha grains are formed from the elongated grains and cold forming properties of CP-Ti were improved. The effect of the first recrystallization annealing was remained. Forming properties were a moderate value for processing 1 due to the presence of equiaxed grains. |
| تدمد: | 1662-9752 |
| DOI: | 10.4028/www.scientific.net/msf.896.193 |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::238ffe571d636fc53f85c5579d8bccb0 https://doi.org/10.4028/www.scientific.net/msf.896.193 |
| Rights: | CLOSED |
| رقم الانضمام: | edsair.doi...........238ffe571d636fc53f85c5579d8bccb0 |
| قاعدة البيانات: | OpenAIRE |
كن أول من يترك تعليقا!